Towards a better understanding of the degradation mechanisms of Li-ion full cells using Si/C composites as anode - Recherche opérationnelle des Systèmes de Production
Article Dans Une Revue Journal of Power Sources Année : 2022

Towards a better understanding of the degradation mechanisms of Li-ion full cells using Si/C composites as anode

Résumé

Carbon-coated silicon nanoparticles (40 nm diameter) were used to prepare pitch-based Si/C composites with different Si contents and a pitch and graphite-based Si/C/Gr composite. These composites were prepared by pyrolysis at 900 °C of a pitch/Si mixture obtained from the dispersion of Si particles in a solution of pitch in THF. The as-prepared composites delivered high coulombic efficiencies at the first cycle (83–86%) and stable reversible capacities (560–650 mAh g−1) versus lithium. The anodes degradation phenomena while cycling versus NMC622 in a full cell configuration were studied by simple electrochemical tests such as analysing the harvested electrodes in half-cells vs. lithium. The clear improvement on electrochemical performances due to the graphite addition was demonstrated with the suppression of the active particle's disconnection. The pitch and graphite-based composite was proven to accommodate well the silicon volume expansion and to deliver a stable electrochemical capacity of 650 mAh g−1 at the rate of C/5.

Domaines

Chimie
Fichier principal
Vignette du fichier
J Power Sources_Gutierrez 2022.pdf (1022.96 Ko) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-03680035 , version 1 (14-11-2022)

Identifiants

Citer

Mariana Gutierrez, Mathieu Morcrette, Laure Monconduit, Yohan Oudart, Pierre Lemaire, et al.. Towards a better understanding of the degradation mechanisms of Li-ion full cells using Si/C composites as anode. Journal of Power Sources, 2022, 533, pp.231408. ⟨10.1016/j.jpowsour.2022.231408⟩. ⟨hal-03680035⟩
125 Consultations
174 Téléchargements

Altmetric

Partager

More