Three scale modeling of the behavior of a 16MND5-A508 bainitic steel: Stress distribution at low temperatures

Résumé

An original approach is proposed to predict the behavior of the16MND5bainitic steel (similar to U.S. A508 cl.3) in the lower range of the ductile-to-brittle transition region and at lower temperatures [−196 ◦C; 20 ◦C], by developing a new polycrystalline modeling concurrently with X-ray diffraction (XRD) analysis. A two-level homogenization is used to take into account each kind of heterogeneity as well as the phase and grain interactions. A Mori–Tanaka formulation first enables to describe the elastoplastic behavior of a bainitic single crystal (modeled as a single crystal ferritic matrix reinforced by cementite inclusions), while the transition to polycrystal is achieved by a self-consistent approach. This model can simulate in particular the effects of temperature. It reproduces qualitatively the stress distribution in the material (stress states are lower in ferrite than in the bulk material due to cementite particles, the difference never exceeding 150 MPa), the intergranular strain heterogeneity (ripples observed on the ε = f(sin2 ) curve) and the pole figures determined by XRD on different scales. The proposed approach is validated here on the macroscopic, phase and intraphase scale.
Fichier principal
Vignette du fichier
LEM3_JMSEA_2009_PESCI.pdf (2.07 Mo) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01166251 , version 1 (02-07-2015)

Identifiants

Citer

Raphaël Pesci, Karim Inal, Renaud Masson. Three scale modeling of the behavior of a 16MND5-A508 bainitic steel: Stress distribution at low temperatures. Materials Science and Engineering: A, 2009, 527 (1-2), pp.376-386. ⟨10.1016/j.msea.2009.08.020⟩. ⟨hal-01166251⟩
210 Consultations
204 Téléchargements

Altmetric

Partager

More